Santos, A.P.R. ; Pereira, G.R. ; ROCHA, A. C. .
Resumo: This work utilizes the electrochemical parameters proposed by the ISO 12732 standard to evaluate the susceptibility to localized corrosion of super duplex stainless steel UNS S32760. The relationship between these electrochemical parameters (ratio of peak currents or charge obtained with activation and reactivation during potentiodynamic polarization) and the percentage by weight of deleterious phases are evaluated. For the aging conditions, the deleterious effect of the phases has been satisfactorily detected by the DL-EPR technique. A new experimental protocol allowed the characterization of the attacks that occurred for each polarization range Neste trabalho, amostras de aço Lean Duplex UNS S32304 foram submetidas à temperatura de 800°C em um forno acoplado a um difratômetro de raios-x durante intervalos de tempo de 30, 60 e 90 minutos. Com o objetivo de analisar em tempo real a transformação das fases constituintes, foram realizadas várias varreduras insitu durante os diferentes tempos de permanência em 800°C deste material. Assim, observou-se a formação da fase sigma neste aço, tanto nos contornos de grão da ferrita como nas interfaces ferrita/austenita. Os valores de fase sigma obtidos para cada tempo de exposição foram calculados através do método de Rietveld sobre cada difratograma obtido e variaram de 11% a 17%. Notou-se que a fase sigma exibiu crescimento contínuo até 60 minutos e variação após este período. Todavia, observou-se que a formação de fase sigma a 800°C ocorre de forma significativa neste material após 30 minutos de aquecimento, o que pode comprometer as propriedades do mesmo.